AM Bench 2022 challenge Macroscale Tensile Tests at Different Orientations (CHAL-AMB2022-04-MaTTO)
National Institute of Standards and Technology —
Additively manufactured (AM) laser powder bed fusion (PBF-L) Inconel 625 blocks were built with two different scan strategies: XY and X-only. 96 tensile specimens... -
Federal
AM Bench 2022 challenge problem Subcontinuum Mesoscale Tensile Test (CHAL-AMB2022-04-MeTT)
National Institute of Standards and Technology —
One additively manufactured (AM) laser powder bed fusion (PBF-L) Inconel 625 mesoscale tensile specimen (gauge dimensions approximately 0.2mm x 0.2 mm x 1mm) was... -
Federal
AM Bench 2022 ASTM E8 Macroscale Tension at Different Strain Rates on As-built IN625
National Institute of Standards and Technology —
Macro-scale tensile data on additively manufactured (AM) IN625 in the as-built microstructural condition at room temperature and at different strain rates are... -
Federal
AM Bench 2022 Residual Elastic Strain, Residual Stress, and Part Deflection Measurements for IN718 3D Builds
National Institute of Standards and Technology —
The following data files include residual elastic strain, residual stress, and part deflection results associated with the 2022 Additive Manufacturing Benchmark test... -
Federal
AM Bench 2018 Residual Elastic Strain Measurements of 3D Additive Manufacturing Builds of IN625 Artifacts Using Neutron Diffraction and Synchrotron X-ray Diffraction
National Institute of Standards and Technology —
The development of large residual elastic strains and stresses during laser powder-bed fusion (LPBF) additive manufacturing is one of the most significant barriers to...