Process-structure-properties investigations for laser powder bed fused IN718 in the as-built condition recent views
National Institute of Standards and Technology —
This data repository provides a central location for a body of work using one build of nickel-based alloy 718 (IN718) material and resulted in three different... -
Federal
Asynchronous AM Bench 2022 Challenge Data: Real-time, simultaneous absorptance and high-speed Xray imaging recent views
National Institute of Standards and Technology —
The absolute laser absorption was measured simultaneously with X-ray imaging during laser melting of Ti-6Al-4V solid metal. The data included here are the time-... -
Federal
Additive Manufacturing Benchmark Test Series (AM-Bench) 2018 Test Descriptions recent views
National Institute of Standards and Technology —
The Additive Manufacturing Benchmark Test Series (AM-Bench) is developing a continuing series of controlled benchmark tests, in conjunction with a conference series,... -
Federal
Hot-wire anemometer gas speed measurements in a commercial laser powder bed fusion machine recent views
National Institute of Standards and Technology —
Gas speed measurements using hot-wire anemometers (HWA) on a commercial laser powder bed fusion (LBPF) machine were recorded as a function of position (X, Y, Z) and... -
Federal
AM Bench 2022 challenge problem Subcontinuum Mesoscale Tensile Test (CHAL-AMB2022-04-MeTT) recent views
National Institute of Standards and Technology —
One additively manufactured (AM) laser powder bed fusion (PBF-L) Inconel 625 mesoscale tensile specimen (gauge dimensions approximately 0.2mm x 0.2 mm x 1mm) was... -
Federal
AM Bench 2022 ASTM E8 Macroscale Tension at Different Strain Rates on As-built IN625 recent views
National Institute of Standards and Technology —
Macro-scale tensile data on additively manufactured (AM) IN625 in the as-built microstructural condition at room temperature and at different strain rates are... -
Federal
Effects of as-built surface with varying number of contour passes on high-cycle fatigue behavior of additively manufactured nickel alloy 718 recent views
National Institute of Standards and Technology —
Abstract (from the manuscript): High cycle fatigue life of laser-powder bed fusion (L-PBF) parts depends on several factors; as-built surfaces, when present, are a... -
Federal
AM Bench 2022 challenge Macroscale Tensile Tests at Different Orientations (CHAL-AMB2022-04-MaTTO) recent views
National Institute of Standards and Technology —
Additively manufactured (AM) laser powder bed fusion (PBF-L) Inconel 625 blocks were built with two different scan strategies: XY and X-only. 96 tensile specimens... -
Federal
AM Bench 2018 Residual Elastic Strain Measurements of 3D Additive Manufacturing Builds of IN625 Artifacts Using Neutron Diffraction and Synchrotron X-ray Diffraction recent views
National Institute of Standards and Technology —
The development of large residual elastic strains and stresses during laser powder-bed fusion (LPBF) additive manufacturing is one of the most significant barriers to... -
Federal
AM Bench 2022: Cross sectional microstructure of single laser tracks produced using different processing conditions and 2D arrays of laser tracks (pads) on solid plates of nickel alloy 718 recent views
National Institute of Standards and Technology —
The following data files include microstructure measurement results associated with the 2022 Additive Manufacturing Benchmark test series (AM Bench 2022) AMB2022-03...