Co-Cure-Ply Resins for High Performance, Large-Scale Structures

Metadata Updated: May 2, 2019

Large-scale composite structures are commonly joined by secondary bonding of molded-and-cured thermoset components. This approach may result in unpredictable joint strengths. In contrast, assemblies made by co-curing, although limited in size by the mold, result in stable structures, and are certifiable for commercial aviation because of structural continuity through the joints. Multifunctional epoxy resins were prepared that should produce fully-cured subcomponents with uncured joining surfaces, enabling them to be assembled by co-curing in a subsequent out-of-autoclave process. Aromatic diamines were protected by condensation with a ketone or aldehyde to form imines. Properties of the amine-cured epoxy were compared with those of commercially available thermosetting epoxy resins and rheology and thermal analysis were used to demonstrate the efficacy of imine protection. Optimum conditions to reverse the protecting chemistry in the solid state using moisture and acid catalysis were determined. Alternative chemistries were also investigated. For example, self-immolative polymers and photo initiated catalysis would be expected to minimize liberation of volatile organic content upon deprotection and avoid residual reactive species that could damage the resin. The Challenge: Airframe manufactures install mechanical fasteners in adhesively bonded joints to comply with federal aviation regulations. An average commercial aircraft contains several miles of adhesively bonded joints and therefore thousands of redundant fasteners. An alternate means of assembling large-scale composite structures to meet federal regulations is needed to realize the ultimate potential of composites to reduce cost and increase aircraft performance. Removing redundant fasteners may reduce the part count by 120,000 parts and the weight of the aircraft by 5000 lbs. (2%). Multi-functional materials to improve flight efficiency and safety are core components of NASA[HTML_REMOVED]s mission and align well with Langley[HTML_REMOVED]s strategic investment plan.The State-of-the-art vs. the proposed method: Large-scale composites structures are prepared by laying up prepreg in a mold and curing it in an autoclave. For thermosetting polymers (e.g. epoxies) the resin reflows upon heating and then undergoes a curing reaction (cross-linking) to form a solid part. If two components are laid-up together and cured simultaneously, this is known as co-curing (see figure). Co-cured assemblies do not require redundant fasteners because the joints are formed seamlessly as the resin re-flows and eventually cures through the formation of new chemical bonds. The use of the co-cure process is limited by the size of the autoclave or oven being used to mold and cure the part. The proposed work will develop a multifunctional epoxy resin that will enable sub-structures to be fully cured while leaving the joining surfaces uncured for assembly in a subsequent, out-of-autoclave, co-cure process. The proposed multifunctional resin, combined with fiber reinforcement, can be used to manufacture composite structures that match the performance of state-of-the-art, mono-functional materials.The Method Details: The proposed material will be prepared by protecting the reactive groups in a commercially available epoxy resin. Specifically, the amine functional groups of an epoxy hardener will be protected by condensation with a ketone to form an imine. The imine protecting groups will not react with epoxide groups, preventing the resin from curing. After the sub-structures are cured, the imine protecting groups will be removed by exposure to water vapor. Once de-protected, the amine groups will react with epoxides to form a solid, epoxy plastic.The Work Package: Initial demonstrations will be limited to small scale reactions (1 to 10 grams of material). Spectroscopic techniques will be used to verify the success of protecting and de-protecting chemistry. The ability of the resin to prevent curing, undergo de-protection, and cure completely will be assessed by thermomechanical analysis. In a subsequent project, the novel resin would be produced in larger quantities and used to make prepreg, which could be used to prepare composite coupons and assess interlaminar fracture toughness.The Risk: Although protecting group chemistry is well known, a significant risk is presented by attempting to introduce new resin systems to aerospace structures. Usually decades of testing and many practical demonstrations are required before new materials are certified for flight. This risk can be reduced by making the minimum possible modification to resin components that are currently in use.

Access & Use Information

Public: This dataset is intended for public access and use. License: U.S. Government Work

Downloads & Resources


Metadata Created Date August 1, 2018
Metadata Updated Date May 2, 2019

Metadata Source

Harvested from NASA Data.json

Additional Metadata

Resource Type Dataset
Metadata Created Date August 1, 2018
Metadata Updated Date May 2, 2019
Publisher Space Technology Mission Directorate
Unique Identifier TECHPORT_34944
Maintainer Email
Public Access Level public
Bureau Code 026:00
Metadata Context
Metadata Catalog ID
Schema Version
Catalog Describedby
Datagov Dedupe Retained 20190501230127
Harvest Object Id 00eca1db-4ffb-47d5-b195-f1ee5ce4ed71
Harvest Source Id 39e4ad2a-47ca-4507-8258-852babd0fd99
Harvest Source Title NASA Data.json
Data First Published 2016-09-01
Homepage URL
Data Last Modified 2018-07-19
Program Code 026:027
Source Datajson Identifier True
Source Hash 302f8d1b9f3e37c0131273494e7c3fde8dcf46bb
Source Schema Version 1.1

Didn't find what you're looking for? Suggest a dataset here.